Preparation of Pd coated anodic alumina membranes for gas separation media

2007

Different procedures of Pd electroless deposition onto anodic alumina membranes were investigated to form a dense metal layer covering pores. The main difficulty was related to the amorphous nature of anodic alumina membranes, determining low chemical stability in solutions at pH > 9, where Pd plating works more efficiently. As a consequence, it was necessary to find the operative conditions allowing Pd deposition without damaging the membrane: to reduce alumina dissolution, the plating bath was buffered at pH 8.5 by addition of either NaHCO 3 or Na 2 B 4 O 7 ·H 2 O. Acceptable conversion of Pd was found after a deposition time of 3 min. Single and multiple deposition steps (each lasting 3 …